夏季高溫高濕環(huán)境對(duì)石膏粉施工提出更高要求，易出現(xiàn)凝結(jié)過快、開裂、強(qiáng)度下降等問題。通過科學(xué)選材、工藝優(yōu)化及環(huán)境控制，可顯著提升夏季石膏粉施工質(zhì)量。

　　The high temperature and high humidity environment in summer puts higher demands on the construction of gypsum powder, which is prone to problems such as rapid setting, cracking, and decreased strength. Through scientific material selection, process optimization, and environmental control, the construction quality of gypsum powder in summer can be significantly improved.

　　一、材料選擇與預(yù)處理

　　1、 Material selection and pretreatment

　　選用專用配方石膏粉：夏季施工應(yīng)選擇添加緩凝劑的石膏粉，延長可操作時(shí)間。某建材實(shí)驗(yàn)室數(shù)據(jù)顯示，緩凝型石膏粉初凝時(shí)間可延長，避免高溫下急速固化。

　　Choose specialized formula gypsum powder: gypsum powder with added retarder should be selected for summer construction to extend the operable time. Data from a certain building materials laboratory shows that the initial setting time of delayed setting gypsum powder can be extended to avoid rapid solidification at high temperatures.

　　控制材料含水率：石膏粉儲(chǔ)存環(huán)境濕度需≤60%，使用前需檢測(cè)含水率。某工地曾因材料受潮，導(dǎo)致批刮后出現(xiàn)氣泡、脫落。

　　Control material moisture content: The humidity of the gypsum powder storage environment should be ≤ 60%, and the moisture content should be tested before use. A certain construction site once experienced bubbles and detachment after scraping due to moisture in the materials.

　　預(yù)混添加劑優(yōu)化：按比例摻入纖維素醚、淀粉醚等保水劑，某工程案例表明，該配方可使石膏層抗裂性提升，空鼓率降低。

　　Optimization of pre mixed additives: Mix cellulose ether, starch ether and other water retaining agents in proportion. A certain engineering case shows that this formula can improve the crack resistance of gypsum layer and reduce the hollowing rate.

　　二、施工環(huán)境調(diào)控

　　2、 Construction environment regulation

　　溫度管理：施工現(xiàn)場(chǎng)溫度宜控制在35℃以下，可通過遮陽網(wǎng)、工業(yè)風(fēng)扇或噴淋系統(tǒng)降溫。某醫(yī)院裝修項(xiàng)目采用霧化噴淋，使作業(yè)面溫度降低。

　　Temperature management: The temperature at the construction site should be controlled below 35 ℃, and can be cooled down through shading nets, industrial fans, or sprinkler systems. A certain hospital decoration project adopts atomized spraying to reduce the temperature of the working surface.

　　濕度控制：相對(duì)濕度保持50-70%為宜，過干易導(dǎo)致失水過快，過濕則延緩固化。某數(shù)據(jù)中心項(xiàng)目通過除濕機(jī)，將濕度控制在標(biāo)準(zhǔn)范圍內(nèi)。

　　Humidity control: It is advisable to maintain a relative humidity of 50-70%. If it is too dry, it can cause rapid dehydration, while if it is too wet, it can delay curing. A data center project uses dehumidifiers to control humidity within the standard range.

　　基層處理：施工前對(duì)墻面灑水潤濕，但避免明水積存。某測(cè)試顯示，基層含水率控制在8-12%時(shí)，石膏層粘結(jié)強(qiáng)度最佳。

　　Grassroots treatment: Before construction, sprinkle water on the wall to moisten it, but avoid the accumulation of visible water. A certain test shows that when the moisture content of the base layer is controlled at 8-12%, the bonding strength of the gypsum layer is optimal.

　　三、施工工藝優(yōu)化

　　3、 Construction process optimization

　　分次薄涂原則：?jiǎn)未闻魏穸取?mm，多層施工間隔≥2小時(shí)。某精裝房項(xiàng)目因單次過厚，導(dǎo)致石膏層收縮開裂。

　　The principle of thin coating in batches: the thickness of a single batch scraping is ≤ 5mm, and the interval between multi-layer construction is ≥ 2 hours. A certain high-end housing project experienced shrinkage and cracking of the gypsum layer due to a single instance of excessive thickness.

　　攪拌技術(shù)要點(diǎn)：采用低速電動(dòng)攪拌器，攪拌時(shí)間控制在3-5分鐘，避免引入過多氣泡。某實(shí)驗(yàn)室對(duì)比發(fā)現(xiàn)，攪拌時(shí)間過長會(huì)使石膏漿體密度下降。

　　Key points of mixing technology: Use a low-speed electric mixer, control the mixing time within 3-5 minutes, and avoid introducing too many bubbles. A laboratory comparison found that excessive mixing time can lead to a decrease in the density of gypsum slurry.

　　收光時(shí)機(jī)把握：在石膏層初凝前完成收光，某技師經(jīng)驗(yàn)分享，以手指輕壓不凹陷但留有指紋時(shí)為最佳收光時(shí)機(jī)。

　　Timing of Light Collection: Complete the light collection before the initial setting of the gypsum layer. A technician shared their experience that the best time for light collection is when the fingers lightly press without sinking but leaving fingerprints.

　　四、特殊部位處理技巧

　　4、 Special part handling techniques

　　陰陽角加固：采用PVC護(hù)角條或網(wǎng)格布增強(qiáng)，某酒店項(xiàng)目應(yīng)用后，陰陽角開裂率降低。

　　Reinforcement of internal and external corners: PVC corner strips or mesh cloth are used for reinforcement. After application in a certain hotel project, the cracking rate of internal and external corners is reduced.

　　管線槽修補(bǔ)：槽內(nèi)先涂刷界面劑，再分層填嵌石膏，每層厚度≤10mm。某案例顯示，該工藝使管線槽區(qū)域平整度提升。

　　Pipeline trench repair: The trench is first coated with interface agent, and then filled with gypsum layer by layer, with a thickness of ≤ 10mm per layer. A certain case shows that this process improves the flatness of the pipeline trench area.

　　頂面施工要點(diǎn)：采用逆光批刮法，利用自然光線檢查平整度，某體育館項(xiàng)目通過該方法，頂面平整度誤差控制在±2mm以內(nèi)。

　　Key points of top surface construction: Adopt the reverse light scraping method and use natural light to check the flatness. A certain sports hall project has controlled the top surface flatness error within ± 2mm through this method.

　　五、養(yǎng)護(hù)與成品保護(hù)

　　5、 Maintenance and finished product protection

　　保濕養(yǎng)護(hù)：施工后24小時(shí)內(nèi)保持環(huán)境濕度≥50%，可采用覆蓋濕麻布或噴水養(yǎng)護(hù)。某實(shí)驗(yàn)室測(cè)試表明，保濕養(yǎng)護(hù)可使石膏強(qiáng)度提升。

　　Moisturizing maintenance: Within 24 hours after construction, maintain an environmental humidity of ≥ 50%, and cover with damp cloth or spray water for maintenance. A laboratory test shows that moisturizing maintenance can increase the strength of gypsum.

　　避免風(fēng)干過快：關(guān)閉門窗，防止穿堂風(fēng)直吹，某住宅項(xiàng)目因開窗通風(fēng)導(dǎo)致石膏層龜裂。

　　Avoid drying out too quickly: Close doors and windows to prevent direct ventilation. A certain residential project caused cracks in the gypsum layer due to opening windows for ventilation.

　　成品保護(hù)期限：石膏層完全固化前禁止觸碰，夏季養(yǎng)護(hù)時(shí)間需延長至7天以上。某寫字樓項(xiàng)目因提前使用，造成墻面劃痕率增加。

　　Finished product protection period: Do not touch before the gypsum layer is completely cured, and the summer curing time should be extended to more than 7 days. Due to early use, the scratch rate on the walls of a certain office building project has increased.

　　六、問題應(yīng)急處理

　　6、 Emergency response to issues

　　速凝處理：若石膏漿體初凝過快，可摻入檸檬酸緩凝劑，但需嚴(yán)格控制用量≤0.5%。

　　Rapid setting treatment: If the initial setting of gypsum slurry is too fast, citric acid retarder can be added, but the dosage should be strictly controlled to ≤ 0.5%.

　　開裂修補(bǔ)：裂縫寬度≤1mm時(shí)，用彈性膩?zhàn)犹钇剑唬?mm時(shí)需切割V型槽后嵌縫處理。

　　Crack repair: When the crack width is ≤ 1mm, fill it with elastic putty; When it is greater than 1mm, a V-shaped groove needs to be cut and then the joint needs to be filled.

　　氣泡處理：批刮后發(fā)現(xiàn)氣泡，需待石膏初凝后鏟除重做，禁止表面壓抹。

　　Bubble treatment: If bubbles are found after scraping, they should be removed and redone after the gypsum has initially set. Surface pressure coating is prohibited.

　　夏季石膏粉施工需構(gòu)建“材料-環(huán)境-工藝”三位一體管控體系，通過精細(xì)化操作與實(shí)時(shí)監(jiān)測(cè)，可有效規(guī)避季節(jié)性質(zhì)量問題。隨著建筑新材料技術(shù)的發(fā)展，未來石膏粉產(chǎn)品將向“環(huán)境自適應(yīng)、智能調(diào)節(jié)”方向升級(jí)，進(jìn)一步提升夏季施工的可靠性與效率。

　　The construction of gypsum powder in summer requires the establishment of a three in one control system of "materials environment technology". Through refined operation and real-time monitoring, seasonal quality problems can be effectively avoided. With the development of new building material technology, gypsum powder products will be upgraded towards "environmental adaptability and intelligent regulation" in the future, further improving the reliability and efficiency of summer construction.

　　本文由濟(jì)南石膏粉友情奉獻(xiàn).更多有關(guān)的知識(shí)請(qǐng)點(diǎn)擊:http://m.daquanq.com.cn真誠的態(tài)度.為您提供為全面的服務(wù).更多有關(guān)的知識(shí)我們將會(huì)陸續(xù)向大家奉獻(xiàn).敬請(qǐng)期待.

　　This article is a friendly contribution from Jinan gypsum powder For more information, please click: http://m.daquanq.com.cn Sincere attitude To provide you with comprehensive services We will gradually contribute more relevant knowledge to everyone Coming soon.