一、膩子產品市場分類體系

1、 Market classification system for putty products

物理狀態分類

Physical state classification

（1）膏狀膩子：預拌型產品，開罐即用，施工便捷但儲存期短（通?！?個月）

(1) Pasty putty: a pre mixed product that can be used immediately after opening the can, with convenient construction but short storage period (usually ≤ 6 months)

（2）粉狀膩子：需現場加水調配，保質期長（通常12-24個月），成本效益高

(2) Powdered putty: needs to be mixed with water on site, has a long shelf life (usually 12-24 months), and is cost-effective

（3）膠配填料：由施工方自行摻膠調配，質量波動大，已逐步被淘汰

(3) Adhesive filling material: The construction party shall mix and adjust the adhesive by themselves, and the quality fluctuates greatly, which has gradually been phased out

（4）水泥基膩子：添加特種水泥的剛性產品，適用于高濕度環境

(4) Cementitious putty: a rigid product with added special cement, suitable for high humidity environments

耐水性能分類

Classification of water resistance performance

（1）耐水膩子：通過GB/T 23455-2009標準檢測，浸水后粘結強度≥0.3MPa

(1) Waterproof putty: tested according to GB/T 23455-2009 standard, with a bonding strength of ≥ 0.3MPa after immersion in water

（2）非耐水膩子：遇水即軟化，僅適用于干燥區域

(2) Non water-resistant putty: softens upon contact with water, only suitable for dry areas

應用場景分類

Application scenario classification

（1）內墻膩子：注重環保性，VOC含量≤80g/L（GB 18582-2020）

(1) Interior wall putty: pay attention to environmental protection, VOC content ≤ 80g/L (GB 18582-2020)

（2）外墻膩子：強調耐候性，需通過抗裂性（裂紋寬度≤0.2mm）和凍融循環（≥25次）測試

(2) Exterior wall putty: emphasizing weather resistance, it needs to pass crack resistance (crack width ≤ 0.2mm) and freeze-thaw cycle (≥ 25 times) tests

功能特性分類

Classification of functional characteristics

（1）彈性膩子：斷裂伸長率≥150%，適用于抗震縫等動態接縫

(1) Elastic putty: fracture elongation ≥ 150%, suitable for dynamic joints such as seismic joints

（2）高彈防水膩子：兼具彈性（伸長率≥200%）與防水（吸水率≤5%）功能

(2) High elasticity waterproof putty: combines elasticity (elongation ≥ 200%) and waterproofing (water absorption ≤ 5%) functions

（3）抗裂膩子：含纖維增強材料，抗開裂性能提升300%

(3) Crack resistant putty: containing fiber-reinforced materials, the crack resistance performance is improved by 300%

二、傳統821膩子的技術缺陷分析

2、 Analysis of Technical Defects in Traditional 821 Putty

結構性能缺陷

Structural performance defects

（1）粘結強度僅0.15-0.2MPa（國家標準要求≥0.3MPa）

(1) The bonding strength is only 0.15-0.2MPa (national standard requires ≥ 0.3MPa)

（2）抗壓強度＜2MPa，極易產生壓潰破壞

(2) Compressive strength<2MPa, prone to crushing and failure

（3）線性收縮率高達0.3%，導致開裂風險

(3) The linear shrinkage rate is as high as 0.3%, leading to a risk of cracking

耐久性問題

Durability issues

（1）在相對濕度＞75%環境下，48小時即出現表層粉化

(1) Surface pulverization occurs within 48 hours in an environment with relative humidity greater than 75%

（2）溫度循環（-20℃~60℃）5次后出現空鼓脫落

(2) After 5 temperature cycles (-20 ℃~60 ℃), hollowing and detachment occurred

（3）與保溫板基層的相容性差，界面應力集中

(3) Poor compatibility with insulation board base layer, interface stress concentration

經濟性弊端

Economic disadvantages

（1）返修率高達35%，平均需2.3次重復施工

(1) The repair rate is as high as 35%, and an average of 2.3 repeated constructions are required

（2）鏟除舊膩子產生建筑垃圾1.2kg/m2

(2) Removing old putty generates construction waste of 1.2kg/m2

（3）界面劑處理增加施工成本18-25元/m2

(3) Interface agent treatment increases construction costs by 18-25 yuan/m 2

三、膩子施工工藝規范

3、 Construction process specification for putty

標準施工流程

Standard construction process

基層處理→界面劑涂布（必要時）→第一遍批刮（厚度≤3mm）→第二遍精找平（厚度≤1mm）→打磨（240-400目砂紙）→底漆涂刷

Base treatment → Interface agent coating (if necessary) → First layer of scraping (thickness ≤ 3mm) → Second layer of fine leveling (thickness ≤ 1mm) → Grinding (240-400 grit sandpaper) → Primer coating

批刮次數準則

Scratch frequency criteria

（1）新建墻體：2遍（總厚度≤4mm）

(1) New wall construction: 2 layers (total thickness ≤ 4mm)

（2）改造墻面：3遍（含找平層，總厚度≤6mm）

(2) Wall renovation: 3 layers (including leveling layer, total thickness ≤ 6mm)

（3）特殊基面：需先做專項處理（如保溫板接縫處需加網格布）

(3) Special base surface: Special treatment is required first (such as adding mesh cloth at the joint of the insulation board)

膠粘劑配比要求

Adhesive ratio requirements

（1）粉狀膩子：水灰比0.4-0.5（重量比）

(1) Powdered putty: water cement ratio 0.4-0.5 (weight ratio)

（2）膠液添加量：固體含量≥8%

(2) Glue addition amount: Solid content ≥ 8%

（3）攪拌后稠度：8-10cm（斯托默粘度計）

(3) Consistency after mixing: 8-10cm (Stomer viscometer)

四、材料缺陷對涂裝體系的影響機制

4、 The Influence Mechanism of Material Defects on Coating System

界面失效模式

Interface Failure Mode

（1）附著力不足：導致涂層系統剝離強度下降＞60%

(1) Insufficient adhesion: resulting in a decrease of coating system peel strength by more than 60%

（2）柔韌性差：使漆膜裂紋擴展速率提高3-5倍

(2) Poor flexibility: increases the crack propagation rate of the paint film by 3-5 times

面漆表現影響

Influence of topcoat performance

（1）耗漆量增加：多孔基層導致吸收量增加30-50%

(1) Increased paint consumption: Porous substrate leads to a 30-50% increase in absorption

（2）色差風險：基層pH＞10時面漆變色概率提升80%

(2) Color difference risk: When the pH of the base layer is greater than 10, the probability of color change in the topcoat increases by 80%

（3）早期失效：膩子層破壞使漆膜壽命縮短50-70%

(3) Early failure: Damage to the putty layer shortens the lifespan of the paint film by 50-70%

五、行業發展趨勢

5、 Industry Development Trends

新型材料應用

Application of New Materials

（1）石膏基膩子：兼具呼吸性與強度（抗折≥2.5MPa）

(1) Gypsum based putty: combines breathability and strength (flexural strength ≥ 2.5MPa)

（2）聚合物改性膩子：粘結強度提升至0.8-1.2MPa

(2) Polymer modified putty: bond strength increased to 0.8-1.2MPa

（3）納米復合膩子：憎水角＞110°，耐污性提升顯著

(3) Nano composite putty: hydrophobicity angle>110 °, significantly improved stain resistance

施工技術革新

Construction technology innovation

（1）機械噴涂：施工效率提高300%，厚度偏差≤0.3mm

(1) Mechanical spraying: construction efficiency increased by 300%, thickness deviation ≤ 0.3mm

（2）薄抹灰系統：總厚度≤2mm，干燥時間縮短50%

(2) Thin plastering system: total thickness ≤ 2mm, drying time reduced by 50%

本文由濟南膩子粉友情奉獻.更多有關的知識請點擊:http://m.daquanq.com.cn真誠的態度.為您提供為全面的服務.更多有關的知識我們將會陸續向大家奉獻.敬請期待.

This article is a friendly contribution from Jinan gypsum powder For more information, please click: http://m.daquanq.com.cn Sincere attitude To provide you with comprehensive services We will gradually contribute more relevant knowledge to everyone Coming soon.